Capacitor with zirconium oxide and method for fabricating the same

ABSTRACT

A capacitor with zirconium oxide and a method for fabricating the same are provided. The method includes: forming a storage node; forming a multi-layered dielectric structure on the storage node, the multi-layered dielectric structure including a zirconium oxide (ZrO 2 ) layer and an aluminum oxide (Al 2 O 3 ) layer; and forming a plate electrode on the multi-layered dielectric structure.

CROSS-REFERENCE TO RELATED APPLICATION

The present patent application is a Divisional of application Ser. No. 12/546,603, filed Aug. 24, 2009, which application is a Divisional of application Ser. No. 11/268,855, filed Nov. 7, 2005, now U.S. Pat. No. 7,592,217, issued Sep. 22, 2009.

FIELD OF THE INVENTION

The present invention relates to a capacitor of a semiconductor device and a method for fabricating the same; and, more particularly, to a capacitor of a semiconductor device capable of securing an intended level of capacitance, a leakage current characteristic and thermal stability and a method for fabricating the same.

DESCRIPTION OF RELATED ARTS

As semiconductor devices have been highly integrated, sizes of unit cells have been greatly reduced and an operation voltage level has been lowered. Thus, a refresh time of a device has been shortened and a soft error had generated frequently. Hence, it is required to develop a capacitor which has a capacitance level greater than 25 fF per cell and is less likely to produce leakage current.

As known, the capacitor capacitance is proportional to the surface area of an electrode and a dielectric constant of a dielectric material and, is inversely proportional to the thickness of a dielectric material, which corresponds to a distance between the electrodes, more particularly, to an equivalent silicon oxide thickness (Tox) of a dielectric material. Thus, it is necessary to employ a dielectric material that has a high dielectric constant and can reduce the equivalent silicon oxide thickness (Tox) to fabricate a capacitor with a high capacitance level, which can be implemented suitably for highly integrated semiconductor devices.

It is limited to use a conventional nitride/oxide (NO) type capacitor for securing the high capacitance level required for highly integrated semiconductor devices. The conventional NO type capacitor generally employs a dielectric material of silicon nitride (Si₃N₄) whose dielectric constant is 7. Thus, a polysilicon-insulator-polysilicon (SIS) type capacitor has been proposed to secure a sufficient level of capacitance. The SIS type capacitor uses dielectric materials that have a dielectric constant higher than that of the silicon nitride. Examples of such dielectric materials are tantalum oxide (Ta₂O₅) whose dielectric constant is 25, lanthanum oxide (La₂O₃) whose dielectric constant is 30 and hafnium oxide (HfO₂) whose dielectric constant is 20.

However, the dielectric material of Ta₂O₅ is prone to leakage current and cannot reduce the equivalent silicon oxide thickness practically less than 30 Å due to an oxide layer formed during a thermal process. The dielectric materials of La₂O₃ and HfO₂ are advantageous on high capacitance because of their high dielectric constant values; however, La₂O₃ and HfO₂ frequently deteriorate durability of a capacitor since La₂O₃ and HfO₂ are very weak to repetitive electric shocks because of an increased level of leakage current and a decreased intensity level of breakdown voltage frequently occurring when the equivalent silicon oxide thickness is decreased to less than 15 Å. Especially, HfO₂ has a lower crystallization temperature than Al₂O₃ does. Thus, when HfO₂ is employed, leakage current increases abruptly while a thermal process is performed at temperature of higher than 600° C.

In the case of polysilicon commonly used as a dielectric material for the SIS type capacitor, polysilicon also has a limitation in securing a high level of conductivity required by highly integrated semiconductor devices. Hence, it has been attempted to use other metals with high conductivity as an electrode material.

As for capacitors which can implemented to a fabrication method of dynamic random access memory (DRAM) devices including micronized metal lines of less than 100 nm, capacitors with metal electrodes and dual or triple dielectric structures have been developed. For instance, a metal-insulator-polysilicon (MIS) type capacitor including a titanium nitride (TiN)-based electrode and a dual dielectric structure of HfO₂/Al₂O₃, and a metal-insulator-metal (MIM) type capacitor including a TiN-based electrode and a triple dielectric structure of HfO₂/Al₂O₃/HfO₂ have been developed.

However, it may be difficult to apply the conventional MIS or MIM type capacitor to devices with sub-70 nm metal lines. Since a multi-layered dielectric structure of the MIS or MIM type capacitor (e.g., HfO₂/Al₂O₃ or HfO₂/Al₂O₃/HfO₂) has the minimum equivalent silicon oxide thickness of 12 Å, it may be difficult to secure a capacitance level greater than 25 fF per cell in DRAM devices with sub-70 nm metal lines.

SUMMARY OF THE INVENTION

It is, therefore, an object of the present invention to provide a capacitor of a semiconductor device, wherein the capacitor can secure a leakage current characteristic and a capacitance level generally required by next generation semiconductor memory products with sub-70 nm metal lines, and a method for fabricating the same.

In accordance with an aspect of the present invention, there is provided a method for fabricating a capacitor, including: forming a storage node; forming a multi-layered dielectric structure on the storage node, the multi-layered dielectric structure including a zirconium oxide (ZrO₂) layer and an aluminum oxide (Al₂O₃) layer; and forming a plate electrode on the multi-layered dielectric structure.

In accordance with another aspect of the present invention, there is provided a method for fabricating a capacitor, including: forming a storage node; performing a plasma nitridation process on a surface of the storage node; forming a ZrO₂ layer on the nitrided storage node; performing a plasma nitridation process on a surface of the ZrO₂ layer, thereby obtaining a nitrided ZrO₂ layer; and forming a plate electrode on the nitrided ZrO₂ layer.

In accordance with still another aspect of the present invention, there is provided a method for fabricating a semiconductor device, including: forming a storage node; forming an Al₂O₃ layer on the storage node; forming a ZrO₂ layer on the Al₂O₃ layer; performing a plasma nitridation on a surface of the ZrO₂ layer, thereby obtaining a dielectric structure including a nitrided ZrO₂ layer and the Al₂O₃ layer; and forming a plate electrode on the dielectric structure.

In accordance with a further another aspect of the present invention, there is provided a method for fabricating a capacitor of a semiconductor device, including: forming a storage node; performing a plasma nitridation process on a surface of the storage node; sequentially forming a first ZrO₂ layer, an Al₂O₃ layer and a second ZrO₂ layer on the nitrided storage node; performing a plasma nitridation process on a surface of the second ZrO₂ layer, thereby obtaining a triple dielectric structure including the first ZrO₂ layer, the Al₂O₃ layer and the nitrided second ZrO₂ layer; and forming a plate electrode on the triple dielectric structure.

In accordance with a further aspect of the present invention, there is provided a capacitor of a semiconductor device, including: a storage node; a multi-layered dielectric structure including a ZrO₂ layer and an Al₂O₃ layer and formed on the storage node; and a plate electrode on the multi-layered dielectric structure.

In accordance with an even further aspect of the present invention, there is provided a capacitor of a semiconductor device, including: a storage node; a ZrO₂ layer formed on the storage node and including a plasma nitrided surface; and a plate electrode formed on the ZrO₂ layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects and features of the present invention will become better understood with respect to the following description of the preferred embodiments given in conjunction with the accompanying drawings, in which:

FIGS. 1A to 1C are cross-sectional views of a capacitor fabricated according to a first embodiment of the present invention for illustrating a method for fabricating the same;

FIG. 2 is a diagram illustrating a capacitor structure in accordance with the first embodiment of the present invention;

FIG. 3 is a diagram illustrating sequential steps of forming a multi-layered dielectric structure including a thin layer of zirconium oxide (ZrO₂) and a thin layer of aluminum oxide (Al₂O₃) on the basis of an atomic layer deposition (ALD) method;

FIG. 4 is a diagram illustrating a capacitor structure in accordance with a second embodiment of the present invention;

FIG. 5 is a diagram illustrating a capacitor structure in accordance with a third embodiment of the present invention;

FIG. 6 is a diagram illustrating a capacitor structure in accordance with a fourth embodiment of the present invention;

FIG. 7 is a diagram illustrating a capacitor structure in accordance with a fifth embodiment of the present invention;

FIGS. 8A to 8C are cross-sectional views of a capacitor fabricated according to a sixth embodiment of the present invention for illustrating a method for fabricating the same;

FIG. 8D is a diagram illustrating sequential steps of fabricating a capacitor in accordance with the sixth embodiment of the present invention;

FIG. 9 is a diagram illustrating sequential steps of fabricating a capacitor in accordance with a seventh embodiment of the present invention;

FIG. 10 is a diagram illustrating sequential steps of fabricating a capacitor in accordance with an eighth embodiment of the present invention; and

FIG. 11 is a diagram illustrating sequential steps of fabricating a capacitor in accordance with a ninth embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

A capacitor with zirconium oxide and a method for fabricating the same in accordance with exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

According to the exemplary embodiments of the present invention, a capacitor with a multi-layered dielectric structure including a plasma nitrided thin zirconium oxide (ZrO₂) or ZrO₂ layer and a thin aluminum oxide (Al₂O₃) layer is suggested to secure a sufficient capacitance level greater than approximately 30 fF per cell required by capacitors of sub-70 nm semiconductor memory devices, e.g., dynamic random access memory (DRAM) devices, a leakage current level less than approximately 0.5 fF per cell and a breakdown voltage level greater than approximately 2.0 V at the condition of approximately 1 pA per cell.

Generally, ZrO₂ has band gap energy (Eg) of approximately 7.8 eV and a dielectric constant of approximately 20 to approximately 25 higher than those of Ta₂O₅ and HfO₂. As a reference, Ta₂O₅ has band gap energy of approximately 4.5 eV and a dielectric constant of approximately 25, and HfO₂ has band gap energy of approximately 5.7 eV and a dielectric constant of approximately 20. Al₂O₃ whose band gap energy and dielectric constant is approximately 8.7 eV and approximately 9 has better thermal stability than HfO₂. Because of these characteristics of ZrO₂ and Al₂O₃, it is exemplified in the following exemplary embodiments of the present invention that a capacitor with a multi-layered dielectric structure including ZrO₂ and Al₂O₃ is advantageous on leakage current and thermal stability compared with a conventional capacitor with a dielectric structure including a single layer.

Hence, the above multi-layered dielectric structure can decrease the equivalent silicon oxide thickness to less than approximately 12 Å and thus, a capacitor with the above multi-layered dielectric structure can secure capacitance of greater than approximately 30 fF per cell in sub-70 nm DRAM devices.

Accordingly, the capacitor with the multi-layered dielectric structure can secure a sufficient capacitance level required by next generation DRAM products with sub-70 nm metal lines as well as leakage current and breakdown voltage characteristics which can be suitably maintained for mass-production.

After the deposition of the thin ZrO₂ layer and the thin Al₂O₃ layer, a low temperature annealing process is performed to improve layer properties, and a high temperature annealing process is performed to improve a crystallization characteristic. To prevent degradation of the leakage current characteristic, Al₂O₃, which has good thermal stability, is used together with a metal electrode.

Hereinafter, a method for fabricating a capacitor including a dielectric structure of Al₂O₃/ZrO₂ in accordance with a first embodiment of the present invention will be described in detail.

FIGS. 1A to 1C are cross-sectional views of a capacitor fabricated according to the first embodiment of the present invention for illustrating a fabrication method thereof.

Referring to FIG. 1A, although not illustrated, a substrate 11 is provided with bottom patterns including transistors and bit lines. An inter-layer insulation layer 12 is formed on the substrate 11 such that the inter-layer insulation layer 12 covers the bottom patterns.

The inter-layer insulation layer 12 is etched and a plurality of contact holes 13 exposing junction regions or landing plug polysilicon (LPP) regions are formed. A conductive material is filled into the plurality of contact holes 13, thereby obtaining a plurality of storage node contacts 14.

A layer of a storage node material is formed over the storage node contacts 14 and the inter-layer insulation layer 12. An isolation process including a chemical mechanical polishing (CMP) process or an etch-back process is performed on the layer of the storage node material to form storage nodes 15 individually connected with the storage node contacts 14. The storage nodes 15 include a material selected from the group consisting of doped polysilicon, titanium nitride (TiN), tantalum nitride (TaN), tungsten (W), tungsten nitride (WN), ruthenium (Ru), ruthenium oxide (RuO₂), iridium (Ir), iridium oxide (IrO₂), platinum (Pt), Ru/RuO₂, Ir/IrO₂, and SrRuO₂ and have a thickness of approximately 200 Å to approximately 500 Å. In addition to a cylinder structure, the storage nodes 15 can be formed in a concave structure or in a simple stack structure.

For instance, if the storage nodes 15 include TiN, titanium tetrachloride (TiCl₄) and ammonia (NH₃) are used as a source material and a reaction gas, respectively. The source material and the reaction gas flow in an amount of approximately 10 sccm to approximately 1,000 sccm. At this time, a chamber is maintained with a pressure of approximately 0.1 torr to approximately 10 torr and a substrate temperature of approximately 500° C. to approximately 700° C. The TiN layer is formed in a thickness of approximately 200 Å to approximately 500 Å.

Afterwards, a low temperature annealing process is performed in an atmosphere of a gas selected from the group consisting of nitrogen (N₂), hydrogen (H₂), N₂/H₂, O₂, O₃, and NH₃ to densify the storage nodes 15, remove impurities remaining inside the storage nodes 15, which become a cause for increasing leakage current, and eliminate surface roughness. Particularly, the smooth surface prevents electric fields from being concentrated at a certain region.

The low temperature annealing process is carried out by using one of a plasma, a furnace and a rapid thermal process (RTP). In the case of using the plasma, the low temperature annealing process is carried out for approximately 1 minutes to approximately 5 minutes under a certain recipe; that is, a plasma with a radio frequency (RF) power of approximately 100 W to approximately 500 W, a temperature of approximately 200° C. to approximately 500° C., a pressure of approximately 0.1 torr to approximately 10 torr, and approximately 5 sccm to approximately 5 slm of the selected ambient gas. In the case of using an electrical furnace, the low temperature annealing process is carried out at a temperature of approximately 600° C. to approximately 800° C. flowing approximately 5 sccm to approximately 5 slm of the selected ambient gas. In the case of using the RTP, the low temperature annealing process is carried out at a chamber maintained with a temperature of approximately 500° C. to approximately 800° C. and an ascending pressure of approximately 700 torr to approximately 760 torr or a descending pressure of approximately 1 torr to approximately 100 torr. At this time, the selected ambient gas flows in an amount of approximately 5 sccm to approximately 5 slm.

Referring to FIG. 1B, a multi-layered dielectric structure 16 including a thin ZrO₂ layer 16A and a thin Al₂O₃ layer 16B is formed on the storage nodes 15. The multi-layered dielectric structure 16 is formed by an atomic layer deposition (ALD) method. Detailed description of the ALD method will be described later with reference to FIG. 3.

Referring to FIG. 1C, a plate electrode 17 is formed on the multi-layered dielectric structure 16. The plate electrode includes a material selected from the group consisting of doped polysilicon, TiN, TaN, W, WN, Ru, RuO₂, Ir, IrO₂, Pt, Ru/RuO₂, Ir/IrO₂, and SrRuO₃. It is exemplified in the first embodiment of the present invention that the plate electrode 17 includes TiN and is formed by employing a chemical vapor deposition (CVD) process or a physical vapor deposition (PVD) process. For instance, the TiN deposition by the CVD process will be the following. A source material includes TiCl₄ and a reaction gas includes NH₃. The source material and the reaction gas flow in an amount of approximately 10 sccm to approximately 1,000 sccm. At this time, the CVD chamber is maintained with a pressure of approximately 0.1 torr to approximately 10 torr and a substrate temperature of approximately 500° C. to approximately 600° C. The TiN layer is deposited in a thickness of approximately 200 Å to approximately 400 Å.

After forming the plate electrode, a protection layer 18 is formed over the plate electrode by an ALD method. The protection layer 18 is one of an oxide layer including a material selected from the group consisting of Al₂O₃, hafnium oxide (HfO₂), tantalum oxide (Ta₂O₅), ZrO₂, titanium oxide (TiO₂), and lanthanum oxide (La₂O₃) or a metal layer including TiN. The protection layer 18 has a thickness of approximately 50 Å to approximately 200 Å.

FIG. 2 is a diagram illustrating the capacitor structure in accordance with the first embodiment of the present invention.

As illustrated, the multi-layered dielectric structure 16 is obtained by sequentially forming the thin ZrO₂ layer 16A and the thin Al₂O₃ layer 16B on the storage node 15, and the plate electrode 17 is formed on the multi-layered dielectric structure 16.

The ZrO₂ layer 16A has a thickness of approximately 5 Å to approximately 100 Å, and the Al₂O₃ layer 16B has a thickness of approximately 5 Å to approximately 30 Å. The total thickness of the multi-layered dielectric structure 16 ranges from approximately 10 Å to approximately 130 Å.

FIG. 3 is a diagram illustrating sequential steps of forming a multi-layered dielectric structure including a thin ZrO₂ layer and a thin Al₂O₃ layer according to an ALD method.

As illustrated, the ZrO₂ layer and the Al₂O₃ layer are deposited through an ALD method, which performs a repetitive unit cycle until intended thicknesses of the above target layers are obtained. The unit cycle includes: supplying a source gas; supplying a purge gas; supplying a reaction gas; and supplying a purge gas. In more detail of the unit cycle, the source gas is supplied to a chamber and is adsorbed onto a target structure. Non-adsorbed portions of the source gas are purged out of the chamber, and the reaction gas is supplied to react with the adsorbed source gas, thereby depositing an intended thin layer. Afterwards, a purge gas is supplied to purge non-reacted portions of the reaction gas out of the chamber.

As for the ZrO₂ deposition, a unit cycle includes: supplying a source gas of Zr; supplying a purge gas; supplying a reaction gas; and supplying a purge gas. This unit cycle is repeated until an intended thickness of the ZrO₂ layer is obtained. At this time, the chamber is maintained with a pressure of approximately 0.1 torr to approximately 1 torr and a low substrate temperature of approximately 200° C. to approximately 350° C.

The Zr source gas is selected from the group consisting of ZrCl₄, Zr(N(CH₃)C₂H₅)₄, Zr(O-tBu)₄, Zr(N(CH₃)₂)₄, Zr(N(C₂H₅)(CH₃))₄, Zr(N(C₂H₅)₂)₄, Zr(TMHD)₄, Zr(OiC₃H₇)₃(TMTD), and Zr(OtBu)₄ and is adsorbed onto a target structure as the Zr source gas is supplied to the chamber. At this time, the Zr source gas is supplied to the chamber with an aid of helium (He) gas serving as a carrier gas. The Ar gas flows in an amount of approximately 150 sccm to approximately 250 sccm for approximately 0.1 seconds to approximately 10 seconds.

Next, a purge gas including nitrogen (N₂) gas or argon (Ar) gas flows into the chamber to purge non-adsorbed portions of the Zr source gas out of the chamber. The purge gas flows in an amount of approximately 200 sccm to approximately 400 sccm for approximately 3 seconds to approximately 10 seconds.

A reaction gas selected from the group consisting of ozone (O₃), oxygen (O₂), O₂ plasma, nitrogen oxide (N₂O), N₂O plasma, and water (H₂O) vapor flows into the chamber and reacts with the adsorbed Zr source gas, thereby depositing the thin ZrO₂ layer. The reaction gas flows in an amount of approximately 0.1 slm to approximately 1 slm for approximately 3 seconds to approximately 10 seconds. If the reaction gas is O₃ gas of which concentration ranges from approximately 100 gcm⁻³ to approximately 500 gcm⁻³, the O₃ gas flows in an amount of approximately 200 sccm to approximately 500 sccm.

A purge gas including N₂ gas or Ar gas flows into the chamber to purge non-reacted portions of the reaction gas out of the chamber. The purge gas flows in an amount of approximately 50 sccm to approximately 200 sccm for approximately 3 seconds to approximately 10 seconds.

The above unit cycle is repeated until the thickness of the ZrO₂ layer is in a range from approximately 5 Å to approximately 100 Å.

After the ZrO₂ deposition, the Al₂O₃ deposition is instigated, and a unit cycle of the Al₂O₃ deposition includes: supplying a source gas of Al; supplying a purge gas; supplying a reaction gas; and supplying a purge gas. This unit cycle is repeated until an intended thickness of the Al₂O₃ layer is obtained. At this time, the chamber is maintained with a pressure of approximately 0.1 torr to approximately 1 torr and a low substrate temperature of approximately 200° C. to approximately 500° C.

The Al source gas selected from the group consisting of Al(CH₃)₃, Al(C₂H₅)₃ and other Al-containing organic metal compounds is adsorbed onto a target structure as the Al source gas is supplied to the chamber for the ALD method. At this time, the Al source gas is supplied to the chamber with an aid of helium (He) gas serving as a carrier gas. The Ar gas flows in an amount of approximately 20 sccm to approximately 100 sccm for approximately 0.1 seconds to approximately 5 seconds.

Next, a purge gas including N₂ gas or Ar gas flows into the chamber to purge non-adsorbed portions of the Al source gas out of the chamber. The purge gas flows in an amount of approximately 50 sccm to approximately 300 sccm for approximately 0.1 seconds to approximately 5 seconds.

A reaction gas selected from the group consisting of O₃, O₂, O₂ plasma, N₂O, N₂O plasma, and H₂O vapor flows in the chamber and reacts with the adsorbed Al source gas, thereby depositing the thin Al₂O₃ layer. The reaction gas flows in an amount of approximately 0.1 slm to approximately 1 slm for approximately 3 seconds to approximately 10 seconds. If the reaction gas is O₃ gas of which concentration ranges from approximately 100 gcm⁻³ to approximately 500 gcm⁻³, the O₃ gas flows in an amount of approximately 200 sccm to approximately 500 sccm.

A purge gas including N₂ gas or Ar gas flows into the chamber to purge non-reacted portions of the reaction gas out of the chamber. The purge gas flows in an amount of approximately 300 sccm to approximately 1,000 sccm for approximately 0.1 seconds to approximately 10 seconds.

The above unit cycle is repeated until the thickness of the Al₂O₃ layer is in a range from approximately 5 Å to approximately 30 Å.

After the deposition of the ZrO₂ layer and the Al₂O₃ layer in-situ, a low temperature annealing process is performed to remove impurities such as carbon and hydrogen and eliminate defects like oxygen apertures and surface roughness, so that leakage current and breakdown voltage characteristics of the aforementioned thin layers can be improved. The low temperature annealing process employs one of a plasma annealing process and ultraviolet (UV)/O₃ annealing process.

The plasma annealing process is performed at a temperature ranging from approximately 300° C. to approximately 450° C. in an atmosphere of a gas selected from the group consisting of N₂, He, N₂/H₂, NH₃, N₂O, N₂/O₂, O₂, and O₃. The selected gas flows in an amount of approximately 100 sccm to approximately 200 sccm for approximately 30 seconds to approximately 120 seconds along with using a plasma with a RF power ranging from approximately 50 W to approximately 300 W and a pressure of approximately 0.1 torr to approximately 1 torr. The UV/O₃ annealing process is performed at a temperature ranging from approximately 300° C. to approximately 400° C. for approximately 2 minutes to approximately 10 minutes with an intensity of approximately 1530 mWcm⁻².

Afterwards, a high temperature annealing process is performed to increase dielectric constants of the ZrO₂ layer and the Al₂O₃ layer. The high temperature annealing process is carried out in an atmosphere of a gas selected from the group consisting of N, Ar and He by employing one of a rapid thermal annealing process and a furnace annealing process. The rapid thermal annealing process is carried out at a temperature of approximately 500° C. to approximately 800° C. within a chamber set with either an ascending pressure of approximately 700 torr to approximately 760 torr or a descending pressure of approximately 1 torr to approximately 100 torr. The selected gas flows in an amount of approximately 5 sccm to approximately 5 slm for approximately 30 seconds to approximately 120 seconds. The furnace annealing process is performed at a temperature of approximately 600° C. to approximately 800° C. for approximately 10 minutes to approximately 30 minutes along with the selected gas flowing in an amount of approximately 5 sccm to approximately 5 slm.

The low temperature annealing process including the plasma annealing process or the UV/O₃ annealing process and the high temperature annealing process including the rapid thermal annealing process or the furnace annealing process can be performed after a plate electrode is formed.

FIG. 4 is a diagram illustrating a capacitor structure in accordance with a second embodiment of the present invention.

The capacitor structure includes: a storage node 21; a multi-layered dielectric structure 22; and a plate electrode 23. Different from the first embodiment, the multi-layered dielectric structure 22 in the second embodiment has a structure of ZrO₂/Al₂O₃ obtained by sequentially stacking an Al₂O₃ layer 22A and a ZrO₂ layer 22B. The ZrO₂ layer 22B has a thickness of approximately 5 Å to approximately 100 Å, while the Al₂O₃ layer 22A has a thickness of approximately 5 Å to approximately 30 Å.

FIG. 5 is a diagram illustrating a capacitor structure in accordance with a third embodiment of the present invention.

The capacitor structure includes: a storage node 31; a multi-layered dielectric structure 32; and a plate electrode 33. The multi-layered dielectric structure 32 has a structure of (Al₂O₃/ZrO₂)_(n), where 2≦n≦10, wherein the alternating sequential deposition of a ZrO₂ layer 32A and an Al₂O₃ layer 32B is repeated at least more than two times. Herein, ‘n’ is the number of deposition of each thin layer. The ZrO₂ layer 32A has a thickness of approximately 5 Å to approximately 25 Å, while the Al₂O₃ layer 32B has a thickness of approximately 5 Å to approximately 10 Å.

FIG. 6 is a diagram illustrating a capacitor structure in accordance with a fourth embodiment of the present invention.

The capacitor structure includes: a storage node 41; a multi-layered dielectric structure 42; and a plate electrode 43. The multi-layered dielectric structure 42 has a structure of (ZrO₂/Al₂O₃)_(n), where 2≦n≦10, wherein the alternating sequential deposition of an Al₂O₃ layer 42A and a ZrO₂ layer 42B is repeated at least more than two times. Herein, ‘n’ is the number of deposition of each thin layer. The ZrO₂ layer 42B has a thickness of approximately 5 Å to approximately 25 Å, while the Al₂O₃ layer 42A has a thickness of approximately 5 Å to approximately 10 Å.

FIG. 7 is a diagram illustrating a capacitor structure in accordance with a fifth embodiment of the present invention.

The capacitor structure includes: a storage node 51; a multi-layered dielectric structure 52; and a plate electrode 53. The multi-layered dielectric structure 52 has a triple-layer structure of ZrO₂/Al₂O₃/ZrO₂, wherein a first ZrO₂ layer 52A, an Al₂O₃ layer 52B and a second ZrO₂ layer 52C are sequentially stacked. The first ZrO₂ layer 52A and the second ZrO₂ layer 52C has a thickness of approximately 5 Å to approximately 50 Å, and the Al₂O₃ layer 52B has a thickness of approximately 5 Å to approximately 15 Å.

As illustrated in FIGS. 4 to 7, the thin Al₂O₃ layer and the thin ZrO₂ layer are deposited by employing the ALD method, and the source gas, the purge gas and the reaction gas for depositing the thin Al₂O₃ layer and the thin ZrO₂ layer are used identically to those gases described in the first embodiment.

Preferably, the Zr source gas is selected from the group consisting of ZrCl₄, Zr(N(CH₃)C₂H₅)₄, Zr(O-tBu)₄, Zr(N(CH₃) ₂)₄, Zr(N(C₂H₅)(CH₃))₄, Zr(N(C₂H₅)₂)₄, Zr(TMHD)₄, Zr(OiC₃H₇)₃(TMTD, and Zr(OtBu)₄. The purge gas includes N₂ gas or Ar gas and the reaction gas is selected from the group consisting of O₃, O₂, O₂ plasma, N₂O, N₂O plasma, and H₂O vapor. The Al source gas is selected from the group consisting of Al(CH₃)₃, Al(C₂H₅)₃ and other Al-containing organic metal compounds.

After the deposition of the ZrO₂ layer and the Al₂O₃ layer in-situ according to the ALD method, a low temperature annealing process is performed to remove impurities such as carbon and hydrogen and eliminate defects like oxygen apertures and surface roughness, so that leakage current and breakdown voltage characteristics of the aforementioned thin layers can be improved. A high temperature annealing process is then performed to increase dielectric constants of the aforementioned thin layers. Recipes for the low temperature annealing process and the high temperature annealing process will be the same as described in the first embodiment of the present invention.

The capacitor structures according to the first embodiment to the fifth embodiment includes a multi-layered dielectric structure including the ZrO₂ layer, which has high band gap energy of approximately 7.8 eV and a dielectric constant of approximately 20 to approximately 25, and the Al₂O₃ layer, which has good thermal stability, band gap energy of approximately 8.7 eV and a dielectric constant of approximately 9. As a result of this specific multi-layered dielectric structure, it is possible to prevent a generation of leakage current and increase a breakdown voltage value. Also, a high level of capacitance can also be secured. Therefore, it is possible to realize capacitors which can have a sufficient capacitance level required by highly integrated memory products with sizes of less than approximately 70 nm and have improved leakage current and breakdown voltage characteristics.

Since the above multi-layered dielectric structure has good thermal stability compared with a dielectric structure including a single dielectric layer such as an HfO₂ layer, electric characteristics are less likely to be deteriorated even during a high temperature process required to be performed in integration processes after the capacitor formation. Accordingly, it is possible to improve durability and reliability of capacitors in next generation semiconductor memory devices implemented with sub-70 nm metal lines.

FIGS. 8A to 8C are cross-sectional views of a capacitor fabricated according to a sixth embodiment of the present invention for illustrating a method for fabricating the same. FIG. 8D is a diagram briefly illustrating sequential steps of a method for fabricating the capacitor according to the sixth embodiment of the present invention.

Referring to FIG. 8A, an inter-layer insulation layer 62 is formed on a substrate 61 on which bottom patterns (not shown) including transistors and bit lines are formed. The inter-layer insulation layer 62 is etched to form a plurality of contact holes 63 exposing junction regions or LPP regions. A conductive material is then filled into the contact holes 63, thereby forming storage node contacts 64. A layer of a storage node material is formed over the inter-layer insulation layer 62 and the storage node contacts 64, and an isolation process employing a CMP process or an etch-back process is performed to form storage nodes 65 individually contacting the storage node contacts 64.

The storage nodes 65 include a material selected from the group consisting of doped polysilicon, TiN, TaN, W, WN, Ru, RuO₂, Ir, IrO₂, Pt, Ru/RuO₂, Ir/IrO₂, and SrRuO₃ and have a thickness ranging from approximately 200 Å to approximately 500 Å. Also, the storage nodes 65 can be formed in a cylinder structure, a concave structure or a simple stack structure.

For instance, if the storage nodes 65 include TiN, TiCl₄ and NH₃ are used as a source material and a reaction gas, respectively. The source material and the reaction gas flow in an amount of approximately 10 sccm to approximately 1,000 sccm. At this time, a chamber is maintained with a pressure of approximately 0.1 torr to approximately 10 torr and a substrate temperature of approximately 500° C. to approximately 700° C. The TiN layer is formed in a thickness of approximately 200 Å to approximately 400 Å.

Afterwards, a low temperature annealing process is performed in an atmosphere of a gas selected from the group consisting of N₂, H₂, N₂/H₂, O₂, O₃, and NH₃ to densify the storage nodes 65, remove impurities remaining inside the storage nodes 65, which become a cause for increasing leakage current, and eliminate surface roughness. Particularly, the smooth surface prevents electric fields from being concentrated at a certain region.

The low temperature annealing process is carried out by using one of a plasma, a furnace and a RTP. In the case of using the plasma, the low temperature annealing process is carried out for approximately 1 minutes to approximately 5 minutes under a certain recipe; a plasma with a radio frequency (RF) power of approximately 100 W to approximately 500 W, a temperature of approximately 200° C. to approximately 500° C., a pressure of approximately 0.1 torr to approximately 10 torr, and approximately 5 sccm to approximately 5 slm of the selected ambient gas. In the case of using an electrical furnace, the low temperature annealing process is carried out at a temperature of approximately 600° C. to approximately 800° C. flowing approximately 5 sccm to approximately 5 slm of the selected ambient gas. In the case of using the RTP, the low temperature annealing process is carried out at a chamber maintained with a temperature of approximately 500° C. to approximately 800° C. and an ascending pressure of approximately 700 torr to approximately 760 torr or a descending pressure of approximately 1 torr to approximately 100 torr. At this time, the selected ambient gas of approximately 5 sccm to approximately 5 slm flows into the chamber.

Referring to FIG. 8B, surfaces of the storage nodes 65 are nitrided using a plasma, and then, approximately 30 Å to approximately 100 Å of a thin ZrO₂ layer 67 is deposited on the storage nodes 65. A surface of the ZrO₂ layer 67 is nitrided using a plasma. Hence, a first plasma nitride layer 66A exists beneath the thin ZrO₂ layer 67 and, as described above, is formed by nitriding the surfaces of the storage nodes 65. On the other hand, a second plasma nitride layer 66B exist on top of the thin ZrO₂ layer 67 and, as described above, is formed by nitriding the surface of the thin ZrO₂ layer 67.

The reason for forming the first plasma nitride layer 66A and the second plasma nitride layer 66B is to secure thermal stability of the ZrO₂ layer 67 and prevent penetration of impurities into the ZrO₂ layer 67. The aforementioned plasma nitridation process is carried out under a specific recipe; that is, a temperature of approximately 200° C. to approximately 500° C., a pressure of approximately 0.1 torr to approximately 10 torr, an ambient gas selected from the group consisting of NH₃, N₂ and N₂/H₂, and a RF power of approximately 100 W to approximately 500 W. The plasma nitridation process is carried out at the chamber in which glow discharge is generated for approximately 5 seconds to approximately 300 seconds.

In the case that the plasma nitridation process is performed before and after the deposition of the ZrO₂ layer 67, it is possible to prevent a diffusion of impurities, which is a source for the leakage current, from a subsequent plate electrode to the ZrO₂ layer 67. Especially, the plasma nitridation process induces a formation of Zr—O—N bonds on top and bottom of the ZrO₂ layer 67 to thereby increase a crystallization temperature of the ZrO₂ layer 67. As a result, the crystallization does not take place even if a high temperature process is performed at above approximately 600° C., further providing effects of preventing a generation of leakage current and increasing breakdown voltage of the dielectric structures of the capacitors.

After the plasma nitridation process, an annealing process employing a RTP or a furnace is performed with controlling a nitrogen concentration accumulated on the surface of the ZrO₂ layer 67, so that electric characteristics of the capacitors can be adjusted. The annealing process is performed at approximately 600° C. to approximately 900° C. in an ascending or descending pressure state.

In addition to the ALD method as described in FIG. 3, the thin ZrO₂ layer 67 can be deposited through employing a metal organic chemical vapor deposition (MOCVD) method or a pulsed CVD method.

As for the ZrO₂ deposition according to the ALD method, a unit cycle includes: supplying a source gas of Zr; supplying a purge gas; supplying a reaction gas; and supplying a purge gas. This unit cycle is repeated until an intended thickness of the ZrO₂ layer is obtained. At this time, the chamber is maintained with a pressure of approximately 0.1 torr to approximately 1 torr and a low substrate temperature of approximately 200° C. to approximately 350° C.

The Zr source gas is selected from the group consisting of ZrCl₄, Zr(N(CH₃)C₂H₅)₄ and other Zr-containing organic metal compounds and is transported by a carrier gas such as Ar gas. The Ar gas flows in an amount of approximately 150 sccm to approximately 250 sccm for approximately 0.1 seconds to approximately 10 seconds. The Zr source gas flows in an amount of approximately 50 sccm to approximately 500 sccm.

The reaction gas is selected from the group consisting of O₃, O₂ and H₂O vapor, and the purge gas includes N₂ gas or Ar gas. The selected O₃ gas has a concentration of approximately 200±20 gcm⁻³. The reaction gas flows in an amount of 0.1 slm to approximately 1 slm for approximately 3 seconds to approximately 10 seconds. Instead of using H₂O vapor, heavy water (D₂O) can be used to eliminate a charge trapping event caused by weak hydrogen bonds within the ZrO₂ layer 67. The heavy water (D₂O) results in formation of an insulation layer, e.g., a metal oxide layer, which have deuterium bonds instead of hydrogen bonds. In this case, reliability of the dielectric layer can be improved. Also, in addition to H₂O vapor and heavy water, the reaction gas can include O₃, O₂, O₂ plasma, N₂O, or N₂O plasma.

After the Zr source gas flows into the chamber, the purge gas flows in an amount of approximately: 200 sccm to approximately 400 sccm, or after the reaction gas flows into the chamber, the purge gas flows in an amount of approximately 50 sccm to approximately 200 sccm. In both of the cases, the purge gas flows for approximately 3 seconds to approximately 10 seconds.

Referring to FIG. 8C, a plate electrode 68 is formed on the thin ZrO₂ layer 67 subjected to the plasma nitridation process before and after the ZrO₂ deposition. The plate electrode 68 includes a material selected from the group consisting of doped polysilicon, TiN, TaN, W, WN, WSi, Ru, RuO₂, Ir, IrO₂, and Pt. Particularly, in the case that the plate electrode 68 is formed of a metal, a silicon nitride layer or a polysilicon layer is formed over the plate electrode 68 as a protection layer 69 for improving structural stability of the capacitors against humidity, temperature or electrical shocks. At this time, the protection layer 69 is formed in a thickness of 200 Å to approximately 1,000 Å.

In the sixth embodiment of the present invention, as mentioned above, the plasma nitridation process is performed before and after the ZrO₂ layer 67 is deposited to induce creation of Zr—O—N bonds on the surface of the ZrO₂ thin layer 67. As a result, a crystallization temperature is increased and diffusion of remaining impurities can be blocked. That is, to overcome the limitation in thermal stability of the ZrO₂ layer, i.e., low crystallization temperature, after the ZrO₂ layer 67 is deposited, the plasma nitridation process is performed on the surface of the ZrO₂ layer 67, inducing Zr—O—N bonds by causing nitrogen to combine with the ZrO₂ layer 67. As a result, it is possible to increase the crystallization temperature of the ZrO₂ layer 67 and prevent diffusion of remaining impurities from the plate electrode 68 or storage nodes 65 to the ZrO₂ layer 67.

Accordingly, according to the sixth embodiment of the present invention, the leakage current characteristic of the ZrO₂ layer 67 can be improved and the breakdown voltage of the ZrO₂ layer 67 can be increased, so that the ZrO₂ layer 67 can have structural stability. By employing the nitrided ZrO₂ layer as the dielectric layer of the capacitor, a sufficient capacitance level and an intended leakage current can be secured. Therefore, the capacitor fabricated according to the sixth embodiment can be applied to sub-70 nm memory products.

Instead of employing a single layer of the ZrO₂ layer 67 for the dielectric structure of the capacitor, it is possible to implement a dual dielectric structure including a nitrided Al₂O₃ layer and a nitrided ZrO₂ layer, another dual dielectric structure including an Al₂O₃ layer and a nitrided ZrO₂ layer, a triple dielectric structure including a ZrO₂ layer, an Al₂O₃ layer, a nitrided ZrO₂ layer, another triple dielectric structure including a nitrided ZrO₂ layer, an Al₂O₃ layer and a nitrided ZrO₂ layer, and a further another triple dielectric structure including a nitrided ZrO₂ layer, a nitrided Al₂O₃ layer and a nitride ZrO₂ layer. These dual or triple dielectric structures including the nitrided ZrO₂ layer can have the same effect to the case of employing the single layer of the nitrided ZrO₂ layer as the dielectric structure.

FIG. 9 is a diagram illustrating sequential steps of a method for fabricating a capacitor in accordance with a seventh embodiment of the present invention.

A dual dielectric structure including a nitrided ZrO₂ layer and a nitrided Al₂O₃ layer is exemplified in the seventh embodiment of the present invention. As illustrated, the Al₂O₃ layer is deposited on a storage node including polysilicon or TiN, and an NH₃ plasma nitridation process is performed on the Al₂O₃ layer. A ZrO₂ layer is then formed on the nitrided Al₂O₃ layer, and an NH₃ plasma nitridation process is performed on the ZrO₂ layer, thereby completing the formation of the dual dielectric structure.

FIG. 10 is a diagram illustrating sequential steps of a method for fabricating a capacitor in accordance with an eighth embodiment of the present invention.

A dual dielectric structure including a nitrided ZrO₂ layer and an Al₂O₃ layer is exemplified in the eighth embodiment of the present invention. As illustrated, an Al₂O₃ layer and a ZrO₂ layer are sequentially deposited on a storage node. An NH₃ plasma nitridation process is performed on the ZrO₂ layer, thereby completing the formation of the dual dielectric structure.

According to the seventh embodiment and the eighth embodiment of the present invention, since the Al₂O₃ layer has relatively better thermal stability than the ZrO₂ layer, it is expected that the dual dielectric structure including the nitrided ZrO₂ layer and the Al₂O₃ layer or the nitrided ZrO₂ layer and the nitrided Al₂O₃ layer has a better leakage current characteristic than the dielectric structure including the single layer of the ZrO₂ layer. Particularly, if the subsequent thermal process is performed at above approximately 850° C., as illustrated in FIG. 9, it would be better to perform the NH₃ plasma nitridation process on the surface of the Al₂O₃ layer prior to depositing the ZrO₂ layer. However, if the thermal process is performed at below approximately 850° C., as illustrated in FIG. 10, the NH₃ plasma nitridation process can be performed after the ZrO₂ layer is deposited without performing the NH₃ plasma nitridation process on the Al₂O₃ layer. The latter case of forming the dual dielectric structure would be sufficient to provide an intended level of thermal stability to the ZrO₂ layer.

FIG. 11 is a diagram illustrating sequential steps of a method for fabricating a capacitor in accordance with a ninth embodiment of the present invention.

A triple dielectric structure including a ZrO₂ layer, an Al₂O₃ layer and a nitrided ZrO₂ layer is exemplified in the ninth embodiment of the present invention. As illustrated, an NH₃ plasma nitridation process is performed on the storage node, and a first ZrO₂ layer, an Al₂O₃ layer and a second ZrO₂ layer are sequentially deposited on the nitrided storage node. The second ZrO₂ layer is then subjected to an NH₃ plasma nitridation process.

Similar to the formation of the ZrO₂ layer, the Al₂O₃ layer can be formed through performing one of an ALD method, a MOCVD method and a pulsed CVD method. As for the ALD method, the Al₂O₃ deposition includes a unit cycle including: supplying an Al source gas; supplying a purge gas; supplying a reaction gas; and supplying a purge. This unit cycle is repeated until an intended thickness of the Al₂O₃ layer is obtained. During the ALD method, the chamber is maintained with a pressure of approximately 0.1 torr to approximately 1 torr along with a relatively low substrate temperature ranging from approximately 200° C. to approximately 500° C.

The Al source gas is selected from the group consisting of Al(CH₃)₃, Al(C₂H₅)₃ and other Al-containing organic metal compounds and is transported by a carrier gas, e.g., Ar gas. The Ar gas flows in an amount of approximately 20 sccm to approximately 100 sccm for approximately 0.1 seconds to approximately 5 seconds.

The reaction gas is selected from the group consisting of O₃, O₂ and H₂O vapor, and the purge gas includes N₂ gas or Ar gas. The selected O₃ gas has a concentration of approximately 200±20 gcm⁻³. After the Al source gas flows into the chamber, the purge gas flows in an amount of approximately 50 sccm to approximately 300 sccm for approximately 0.1 seconds to approximately 5 seconds. However, after the reaction gas flows into the chamber, the purge gas flows in an amount of approximately 300 sccm to approximately 1,000 sccm for approximately 0.1 seconds to approximately 10 seconds. The Al source gas flows in an amount of approximately 50 sccm to approximately 500 sccm, and the reaction gas flows in an amount of approximately 0.1 slm to approximately 1 slm for approximately 3 seconds to approximately 10 seconds.

Although the triple dielectric structure including the ZrO₂ layer, the Al₂O₃ layer and the nitrided ZrO₂ layer is exemplified in the ninth embodiment of the present invention, it is still possible to implement a triple dielectric structure including a nitrided ZrO₂ layer, an Al₂O₃ layer and a nitrided ZrO₂ layer or including a nitrided ZrO₂ layer, a nitrided Al₂O₃ layer and a nitrided ZrO₂ layer.

According to the sixth to the ninth embodiments of the present invention, after the ZrO₂ layer is deposited, the surface of the ZrO₂ layer is subjected to the plasma nitridation process, which induces Zr—O—N bonds by combining nitrogen with the ZrO₂ layer. Through this process, the ZrO₂ layer has an increased crystallization temperature and an event of impurity diffusion from the plate electrode or storage node to the ZrO₂ layer can be blocked.

The capacitor dielectric structure can be formed in a single layer of a nitrided ZrO₂ layer, double layers of a nitrided ZrO₂ layer and an Al₂O₃ layer or triple layers of a ZrO₂ layer, an Al₂O₃ layer and a nitrided ZrO₂ layer. As a result, it is possible to secure a sufficient level of capacitance required by sub-100 nm memory products and improve the leakage current characteristic.

According to the first embodiment to the ninth embodiment of the present invention, a multi-layered dielectric structure is formed. The multi-layered dielectric structure includes a ZrO₂ layer, which has a high level of band gap energy of approximately 7.8 eV and a high dielectric constant of approximately 20 to approximately 25, and an Al₂O₃ layer, which has good thermal stability, a high level of band gap energy of approximately 8.7 eV and a dielectric constant of approximately 9. Such multi-layered dielectric structure can prevent a generation of undesired leakage current and increase a breakdown voltage. Also, it is possible to secure high capacitance and thus, it is further possible to implement capacitors with a sufficient capacitance level required by sub-70 nm memory products and improved leakage current and breakdown voltage characteristics.

In respect of the fact that the multi-layered dielectric structure has better thermal stability than a conventional dielectric structure including an HfO₂ layer, degradation of an electric characteristic can be impeded even if a high temperature process is performed in subsequent integration processes. Therefore, durability and reliability of capacitors can be enhanced even in next generation semiconductor memory devices with metal lines of less than approximately 70 nm.

Also, a ZrO₂ layer serving as a dielectric layer of a capacitor is subjected to a plasma nitridation process before and after the ZrO₂ deposition for the purpose of inducing Zr—O—N bonds on the ZrO₂ layer. The creation of the Zr—O—N bonds increases a crystallization temperature of the ZrO₂ layer and prevents an incidence of impurity diffusion from a plate electrode or storage node to the ZrO₂ layer, so that an intended level of capacitance and improved leakage current and breakdown voltage characteristics can be obtained.

Also, the capacitor with the ZrO₂ layer can lower a frequency of generating leakage current during a high temperature process performed at above approximately 700° C., by approximately 2-fold. Accordingly, durability and reliability of the capacitors in highly integrated semiconductor devices can be improved.

The present application contains subject matter related to the Korean patent application No. KR 2004-0090418 and the Korean patent application No. KR 2005-0057692, filed in the Korean Patent Office on Nov. 8, 2004, and on Jun. 30, 2005, respectively, the entire contents of which being incorporated herein by reference.

While the present invention has been described with respect to certain preferred embodiments, it will be apparent to those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the invention as defined in the following claims. 

1. A capacitor of a semiconductor device, comprising: a storage node; a multi-layered dielectric structure including a ZrO₂ layer and an Al₂O₃ layer and formed on the storage node, the ZrO2 layer including a plasma nitrided surface thereon; a plate electrode on the multi-layered dielectric structure; and a protection layer on the plate electrode.
 2. The capacitor of claim 1, wherein the multi-layered dielectric structure has a dual structure of ZrO₂/Al₂O₃ obtained by sequentially stacking a ZrO₂ layer and an Al₂O₃ layer.
 3. The capacitor of claim 2, wherein the ZrO₂ layer has a thickness of approximately 5 Å to approximately 100 Å and the Al₂O₃ layer has a thickness of approximately 5 Å to approximately 30 Å.
 4. The capacitor of claim 1, wherein the multi-layered dielectric structure has a dual structure of Al₂O₃/ZrO₂ obtained by sequentially stacking an Al₂O₃ layer and a ZrO₂ layer.
 5. The capacitor of claim 4, wherein the ZrO₂ layer has a thickness of approximately 5 Å to approximately 100 Å and the Al₂O₃ layer has a thickness of approximately 5 Å to approximately 30 Å.
 6. The capacitor of claim 1, wherein the multi-layered dielectric structure has a triple structure of ZrO₂/Al₂O₃/ZrO₂ obtained by sequentially stacking a first ZrO₂ layer, an Al₂O₃ layer and a second ZrO₂ layer.
 7. The capacitor of claim 6, wherein each of the first ZrO₂ layer and the second ZrO₂ layer has a thickness of approximately 5 Å to approximately 50 Å and the Al₂O₃ layer has a thickness of approximately 5 Å to approximately 15 Å.
 8. The capacitor of claim 1, wherein the multi-layered dielectric structure has a multi-layered structure of (ZrO₂/Al₂O₃)n obtained by forming the Al₂O₃ layer and the ZrO₂ layer alternately at least more than two times.
 9. The capacitor of claim 8, wherein the ZrO₂ layer has a thickness of approximately 5 Å to approximately 25 Å, and the Al₂O₃ layer has a thickness of approximately 5 Å to approximately 10 Å.
 10. The capacitor of claim 8, wherein ‘n’ is in a range of a value greater than or equal to approximately 2 and less than or equal to approximately
 10. 11. The capacitor of claim 1, wherein the multi-layered dielectric structure has a multi-layered structure of (Al₂O₃/ZrO₂)n obtained by forming the ZrO₂ layer and the Al₂O₃ layer alternately at least more than two times.
 12. The capacitor of claim 11, wherein the ZrO₂ layer has a thickness of approximately 5 Å to approximately 25 Å, and the Al₂O₃ layer has a thickness of approximately 5 Å to approximately 10 Å.
 13. The capacitor of claim 11, wherein ‘n’ is in a range of a value greater than or equal to approximately 2 and less than or equal to approximately
 10. 14. The capacitor of claim 1, wherein the protection layer is formed with one of an oxide layer including a material selected from the group consisting of Al₂O₃, hafnium oxide (HfO₂), tantalum oxide (Ta₂O₅), ZrO₂, titanium oxide (TiO₂), and lanthanum oxide (La₂O₃) and a metal layer including TiN and has a thickness of approximately 50 Å to approximately 200 Å.
 15. A capacitor of a semiconductor device, comprising: a storage node; an Al₂O₃ layer formed on the storage node; a ZrO₂ layer formed on the Al₂O₃ layer and including a plasma nitrided surface; and a plate electrode formed on the ZrO₂ layer.
 16. A capacitor of a semiconductor device, comprising: a storage node; an Al₂O₃ layer including a plasma nitrided surface and formed on the storage node; a ZrO₂ layer formed on the Al₂O₃ layer and including a plasma nitrided surface; and a plate electrode formed on the ZrO₂ layer.
 17. A capacitor of a semiconductor device, comprising: a storage node; a dual structure including an Al₂O₃ layer of which surface is plasma nitrided and a first ZrO₂ layer of which surface is plasma nitrided and formed on the storage node; a second ZrO₂ layer formed on the dual structure and including a plasma nitrided surface; and a plate electrode formed on the second ZrO₂ layer.
 18. A capacitor of a semiconductor device, comprising: a storage node; a dual structure including an Al₂O₃ layer and a first ZrO₂ layer of which surface is plasma nitrided and formed on the storage node; a second ZrO₂ layer formed on the dual structure and including a plasma nitrided surface; and a plate electrode formed on the second ZrO₂ layer.
 19. A capacitor of a semiconductor device, comprising: a storage node; a dual structure including an Al₂O₃ layer and a first ZrO₂ layer and formed on the storage node; a second ZrO₂ layer formed on the dual structure and including a plasma nitrided surface; and a plate electrode formed on the second ZrO₂ layer, wherein the dual structure and second ZrO₂ layer form a triple structure of ZrO₂/Al₂O₃/ZrO₂.
 20. The capacitor of claim 19, wherein a surface of the storage node is plasma nitrided. 